PTA Equipment | PTA Weld Deposition
 |
|
Packaging of PTA powders
|
Deloro Stellite powders are gas atomised powders. PTA and laser hardfacing powders are available in these standard size ranges:
|
WM
|
180/53µm
|
|
WE
|
180/63µm
|
|
W
|
150/45µm
|
|
E
|
150/63µm (150/53µm can also be supplied)
|
|
G
|
125/38µm
|
|
HD
|
250/45µm
|
Please see the table below for details of our PTA & Laser powders. Note – the hardness of the weld deposit may vary from that provided depending upon the process parameters and extent of dilution.
|
ALLOY
|
NOMINAL ANALYSIS OF POWDER
|
|
UNS
|
Hardness (HRC)
|
|
Co
|
Cr
|
W
|
C
|
Ni
|
Mo
|
Fe
|
Si
|
Others
|
|
COBALT BASE ALLOY GAS ATOMIZED POWDERS
|
|
Stellite 1
|
Bal.
|
30
|
13
|
2.5
|
<2.0
|
<1.0
|
<2.0
|
<2.0
|
<1.0
|
R30001
|
51-60
|
|
Stellite 4
|
Bal.
|
30
|
13.5
|
0.7
|
<2.5
|
<1.0
|
<2.5
|
<1.0
|
<1.0
|
R30404
|
40-50
|
|
|
Bal.
|
28.5
|
4.6
|
1.2
|
<2.0
|
<1.0
|
<2.0
|
<2.0
|
<1.0
|
R30106
|
40-46
|
|
Stellite 6LC
|
Bal.
|
29
|
4.5
|
1.11
|
<2.0
|
<1.0
|
<2.0
|
<2.0
|
<1.0
|
-
|
38-44
|
|
Stellite 6HC
|
Bal.
|
28.5
|
4.6
|
1.35
|
<2.0
|
<1.0
|
<2.0
|
<2.0
|
<1.0
|
-
|
43-53
|
|
Stellite 156
|
Bal.
|
28
|
4
|
1.7
|
<2.0
|
<1.0
|
<0.5
|
<2.0
|
<1.0
|
-
|
46-54
|
|
|
Bal.
|
30
|
8.5
|
1.45
|
<2.0
|
<1.0
|
<2.0
|
<2.0
|
<1.0
|
R30012
|
43-53
|
|
Stellite 20
|
Bal.
|
32.5
|
17.5
|
2.55
|
<2.0
|
<1.0
|
<2.0
|
<1.0
|
<1.0
|
-
|
52-62
|
|
Stellite 21
|
Bal.
|
27.5
|
-
|
0.25
|
2.6
|
5.4
|
<2.0
|
<2.0
|
<1.0
|
R30021
|
27-40 *
|
|
Stellite 22
|
Bal.
|
28
|
-
|
0.30
|
1.5
|
12
|
<3.0
|
<2.0
|
<0.5
|
-
|
41-49 *
|
|
Stellite 25
|
Bal.
|
20
|
15
|
0.1
|
10
|
<1.0
|
2
|
<1.0
|
1.9%Mn
|
-
|
20-45 *
|
|
Stellite 31
|
Bal.
|
26
|
7.5
|
0.5
|
10.5
|
<1.0
|
<2.0
|
<1.0
|
<0.5
|
R30031
|
20-35 *
|
|
Stellite F
|
Bal.
|
26
|
12.5
|
1.8
|
22
|
<1.0
|
<2.0
|
1.1
|
<0.5
|
R30002
|
40-45
|
| Stellite 157 |
Bal. |
22 |
4.5 |
0.1 |
- |
- |
- |
1.6 |
2.6%B |
- |
54 |
| Stellite 158 |
Bal. |
26 |
5.5 |
0.8 |
- |
- |
- |
1.2 |
0.7%B |
- |
46 |
|
|
Bal.
|
26
|
14
|
3.4
|
<2.0
|
<1.0
|
<2.0
|
<1.0
|
<1.0
|
R30014
|
55-60
|
| Stellite 238 |
Bal. |
26 |
- |
0.1 |
- |
3.0 |
20 |
- |
<1.0 |
- |
20-25 |
|
Stellite 250
|
Bal.
|
28
|
-
|
0.10
|
<1.0
|
<1.0
|
20
|
0.75
|
<1.0
|
-
|
20-28
|
| Stellite 251 |
Bal. |
28 |
<1.0 |
0.28 |
<1.0 |
<1.0 |
18 |
0.75 |
2%Nb |
- |
25-35 |
|
Stellite 306
|
Bal.
|
25
|
3
|
0.55
|
6
|
-
|
<2.5
|
<2.0
|
7%Nb
|
-
|
34-41
|
|
Stellite 694
|
Bal.
|
28.5
|
19.5
|
0.9
|
5
|
-
|
<3.0
|
<1.0
|
1% V
|
-
|
46-52
|
|
Stellite 706
|
Bal.
|
29
|
-
|
1.25
|
<2.0
|
4.5
|
<2.0
|
<1.0
|
<1.0
|
-
|
39-44
|
|
Stellite 712
|
Bal.
|
29
|
-
|
2.0
|
<2.0
|
8.5
|
<2.0
|
<1.0
|
<1.0
|
-
|
46-53
|
| Stellite 2006 |
Bal. |
31 |
- |
1.3 |
8 |
8 |
18 |
1.0 |
- |
- |
44 |
| Stellite 2012 |
Bal. |
33 |
- |
1.7 |
8 |
10 |
15 |
1.5 |
- |
- |
50 |
| Stellite SF1 |
Bal. |
19 |
13 |
1.3 |
14 |
- |
- |
3 |
2.5%B |
|
55 |
| Stellite SF6 |
Bal. |
19 |
7.5 |
0.7 |
14 |
- |
- |
2.5 |
1.5%B |
|
44 |
| Stellite SF12 |
Bal. |
19 |
9 |
0.9 |
14 |
- |
- |
3 |
2.5%B |
|
48 |
| Stellite SF20 |
Bal. |
19 |
15 |
1.5 |
14 |
- |
- |
3 |
3.0%B |
|
60 |
|
ULTIMET
|
Bal.
|
26
|
2
|
0.07
|
9.4
|
5
|
3
|
<1.0
|
<1.0
|
R31233
|
20-45 *
|
|
COBALT BASE TRIBALOY® ALLOYS (GAS ATOMIZED POWDERS)
|
|
T-400
|
Bal.
|
8.5
|
-
|
<0.08
|
<1.5
|
29
|
<1.5
|
2.8
|
<1.0
|
R30400
|
51-57
|
|
T-400C
|
Bal.
|
14
|
-
|
< 0.08
|
<1.5
|
27
|
<1.5
|
2.6
|
<1.0
|
-
|
51-57
|
|
T-401
|
Bal.
|
17
|
-
|
0.2
|
<1.5
|
22
|
<1.5
|
1.3
|
<1.0
|
-
|
45-50
|
|
T-800
|
Bal.
|
17
|
-
|
< 0.08
|
< 1.5
|
29
|
<1.5
|
3.7
|
<1.0
|
-
|
53-61
|
|
T-900
|
Bal.
|
18
|
-
|
< 0.08
|
16
|
23
|
<1.5
|
2.8
|
<1.0
|
-
|
48-5
|
|
ALLOY
|
NOMINAL ANALYSIS OF POWDER
|
|
UNS
|
Hardness (HRC)
|
|
Co
|
Cr
|
W
|
C
|
Ni
|
Mo
|
Fe
|
Si
|
Others
|
|
NICKEL BASE SUPERALLOYS (GAS ATOMIZED POWDERS)
|
|
Nistelle “Super C”
|
-
|
23
|
-
|
0.1
|
Bal.
|
18
|
<1.0
|
<1.0
|
-
|
-
|
15-25 *
|
|
Nistelle C
|
-
|
17
|
4.5
|
0.1
|
Bal.
|
17
|
6
|
<1.0
|
0.3% V
|
-
|
17-27 *
|
|
Nistelle C4C
|
-
|
16
|
-
|
-
|
Bal.
|
16
|
<1.0
|
<1.0
|
-
|
N06455
|
|
|
Nistelle C22
|
<2.0
|
21.5
|
3
|
-
|
Bal.
|
13.5
|
4
|
-
|
0.15% V
|
-
|
|
|
Nistelle C276
|
-
|
15.5
|
3.7
|
-
|
Bal.
|
16
|
5.5
|
<1.0
|
0.15% V
|
-
|
|
|
Nistelle X
|
1.5
|
22
|
<1.0
|
0.15
|
Bal.
|
9.1
|
18.5
|
<1.0
|
<1.0%
|
N06002
|
|
|
Nistelle 305
|
-
|
42
|
-
|
-
|
Bal.
|
-
|
-
|
0.5
|
<1.0%
|
-
|
|
|
Nistelle 2315
|
-
|
20
|
-
|
-
|
Bal.
|
-
|
-
|
<1.0
|
<1.0%
|
-
|
|
|
Nistelle 600
|
-
|
15.5
|
-
|
-
|
Bal.
|
-
|
8
|
<0.5
|
<1.0%
|
N06600
|
|
|
Nistelle 625
|
-
|
21.5
|
-
|
<0.10
|
Bal.
|
9
|
<1.0
|
<0.5
|
3.5% Nb
|
N06625
|
|
|
Nistelle 718
|
<2.0
|
21.5
|
3
|
-
|
Bal.
|
13.5
|
4
|
-
|
0.15% V
|
N07718
|
|
|
ALLOY
|
NOMINAL ANALYSIS OF POWDER
|
|
UNS
|
Hardness (HRC)
|
|
Co
|
Cr
|
W
|
C
|
Ni
|
Mo
|
Fe
|
Si
|
Others
|
| NICKEL BASE HARDFACING ALLOYS (GAS ATOMIZED POWDERS) |
|
|
-
|
-
|
-
|
<0.05
|
Bal.
|
-
|
<1.0
|
2.5
|
1.4%B
|
-
|
20-22
|
|
Deloro 30
|
-
|
9
|
-
|
0.2
|
Bal.
|
-
|
2.3
|
3.2
|
1.2%B
|
-
|
27-31
|
|
Deloro 38
|
-
|
-
|
-
|
0.05
|
Bal.
|
-
|
0.5
|
3.0
|
2.1%B
|
-
|
35-39
|
|
Deloro 40
|
-
|
7.5
|
-
|
0.3
|
Bal.
|
-
|
2.5
|
3.5
|
1.7% B
|
N99644
|
38-42
|
|
Deloro 45
|
-
|
9
|
-
|
0.35
|
Bal.
|
-
|
2.5
|
3.7
|
1.9%B
|
-
|
44-47
|
|
Deloro 46
|
-
|
-
|
-
|
0.05
|
Bal.
|
-
|
-
|
3.7
|
1.9%B
|
-
|
32-40
|
|
Deloro 50
|
-
|
11
|
-
|
0.45
|
Bal.
|
-
|
3.3
|
3.9
|
2.3% B
|
N99645
|
48-52
|
|
Deloro 55
|
-
|
12
|
-
|
0.6
|
Bal.
|
-
|
4.0
|
4.0
|
2.7% B
|
-
|
52-57
|
|
Deloro 60
|
-
|
15
|
-
|
0.7
|
Bal.
|
-
|
4.0
|
4.4
|
3.1% B
|
N99646
|
57-62
|
|
Extrudalloy 50
|
15
|
21
|
-
|
1.3
|
Bal.
|
6
|
<1.0
|
3.0
|
2.3%B
|
-
|
-
|
|
NICKEL BASE TRIBALOY® ALLOYS (GAS ATOMIZED POWDERS)
|
|
T-700
|
<1.5
|
16
|
-
|
< 0.08
|
Bal.
|
32
|
<1.5
|
3.4
|
<1.0
|
-
|
45-52
|
IRON BASE HARDFACING ALLOYS (GAS ATOMIZED POWDERS)
|
ALLOY
|
Fe
|
Cr
|
C
|
Co
|
Mn
|
Mo
|
Nb
|
Ni
|
Si
|
UNS
|
Hardness
(HRC)
|
|
Delcrome 90
|
Bal.
|
27
|
2.9
|
-
|
0.5
|
-
|
-
|
-
|
0.7
|
-
|
55
|
|
Delcrome 92
|
Bal.
|
-
|
3.8
|
-
|
0.5
|
10
|
-
|
-
|
0.6
|
-
|
60
|
|
Delcrome 253
|
Bal.
|
28
|
1.75
|
-
|
0.5
|
4.5
|
-
|
16.5
|
1.3
|
S68000
|
36
|
|
Delcrome 316
|
Bal.
|
17
|
0.05
|
-
|
0.4
|
2.6
|
-
|
11
|
2.5
|
-
|
<20
|
|
Delcrome 316L
|
Bal.
|
18
|
0.03
|
-
|
0.7
|
2.6
|
-
|
13
|
1.8
|
-
|
<20
|
|
Delcrome 6272
|
Bal.
|
25
|
25
|
-
|
-
|
7
|
-
|
14
|
1.8
|
-
|
44
|
|
Norem 02
|
Bal.
|
25
|
1.25
|
-
|
4.5
|
2
|
-
|
4
|
3.4
|
-
|
40
|
|
Tristelle TS-1
|
Bal.
|
30
|
1
|
12
|
-
|
-
|
-
|
10
|
5
|
-
|
38
|
|
Tristelle TS-2
|
Bal.
|
35
|
2
|
12
|
-
|
-
|
-
|
10
|
5
|
-
|
38
|
|
Tristelle TS-3
|
Bal.
|
35
|
3
|
12
|
-
|
-
|
-
|
10
|
5
|
-
|
50
|
|
Tristelle 5183
|
Bal.
|
21
|
2
|
-
|
-
|
-
|
7.5
|
10
|
5
|
-
|
40
|
|
CARBIDES IN A CORROSION RESISTANT HARD ALLOY MATRIX
|
|
Super Stelcar 9365
|
WC in an alloy matrix
|
|
Super Stelcar 50 plus
|
WC in a Deloro 50 alloy matrix
|
|
Super Stelcar 60 plus
|
WC in a Deloro 60 alloy matrix
|
-
Nominal analysis is a guideline only for standard product, does not include all incidental elements and may differ depending on the exact specification/standard used when ordering.
Undiluted weld metal
-
Nominal analysis is a guideline only for standard product, does not include all incidental elements and may differ depending on the exact specification/standard used when ordering.
* depending on the degree of work hardening