Nominal Composition (Mass %) and Physical Properties
Co | Cr | W | Ni | C | Others | Hardness | Density (deposit) | Melting Range |
Base | 28.5 | 19.5 | 5.0 | 0.9 | V, Fe, Si, Mn | 44-50 HRC | 9.02 g/cm3 0.326 lb/in3 |
1237-1296ºC 2259-2365ºF |
Co | Cr | W | Ni | C | Others | Hardness | Density (deposit) | Melting Range |
Base | 28.5 | 19.5 | 5.0 | 0.9 | V, Fe, Si, Mn | 44-50 HRC | 9.02 g/cm3 0.326 lb/in3 |
1237-1296ºC 2259-2365ºF |
Stellite cobalt-based alloys consist of complex carbides in an alloy matrix. They are resistant to wear, galling, and corrosion and retain these properties at high temperatures. Their exceptional wear resistance is due mainly to the unique inherent characteristics of the hard carbide phase dispersed in a CoCr alloy matrix.
Stellite 694 is a cobalt-chromium alloy which has a high tungsten content to ensure high matrix strength at elevated temperatures (up to 1148oC or 2100oF). This alloy exhibits good resistance to wear, creep, erosion, thermal fatigue, and oxidation. The principal application is for hard-facing turbine blade interlock surfaces. Used in gas turbine parts where a higher hardness than Stellite 31 is required.
SPECIFICATION | PRODUCT FORM |
B50TF55 | Solid Wire |
Models
. Please enter the desired qty for the material(s) you want to include in your promotion or Proceed Without Promotion and only your base materials will be added to the cart.
Minimum quantity should be
SAP Material Number | ISO Catalog Number | Grade |
---|
Thank you for your registration, pending approval & completion of the registration, your access is currently limited. Full utilization of product search capabilities & collaboration space is available and will remain. Please allow 2 business days for registration completion.
Thank you for your successful registration. You now have immediate access to log in and utilize the site.
You are about to leave the Solution building process.
Are you sure you want to leave?